Grinding ball
Chrome grinding ball is mainly used inthermal
power,mining,building materials and other industries
by crushing and grinding materials, in the use of the process,the ball will further improve its surface hardness,wear resistance.
while improving the mill production capacity,high wear resistance,also maintain performance over long periods of time.
It not only improves the grinding efficiency,reduces the time of stopping the grinding machine for selection and adding of the balls,but also extends the clearance
cycle,reducesthe labor intensity,and has important
significance for improving the output of themill,
ensuringthe quality of the abrasive,and reducing the consumption of power consumption and the grinding media.
Chengda can provide diameter 4.6mm-140mm and the chrome content ranges from 0.8%-28%,which can be customized according to different needs of users.
Steel forging
Steel forging is a kind of wear-resistant material, the chemical composition is similar to the grinding ball,steel forging is divided into double plane and bispherical(capsule type),mainly used in the ball mill fine grinding silo,it can withstand high frequency of strong impact force and friction,with fine grinding effect,high wear resistance,low crushing rate characteristics,effectively reduce production costs.
Chromiun Alloy Grinding Steel Balls Chemical Components
Designation |
Chemical Composition(%) |
C |
Si |
Mn |
Cr |
Mo |
Cu |
Ni |
P |
S |
ZQCr26 |
2.0-2.6 |
≤1.0 |
0.3-1.5 |
23.0-27.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤0.06 |
≤0.06 |
ZQCr20 |
2.0-2.6 |
≤1.0 |
0.3-1.5 |
18.0-23.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤0.06 |
≤0.06 |
ZQCr15 |
2.0-2.6 |
≤1.0 |
0.3-1.5 |
14.0-18.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤0.06 |
≤0.06 |
ZQCr12 |
2.2-3.0 |
≤1.0 |
0.3-1.5 |
10.0-14.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤0.06 |
≤0.06 |
ZQCr8 |
2.2-3.0 |
≤1.0 |
0.3-1.5 |
7.0-10.0 |
≤1.0 |
≤0.8 |
≤1.0 |
≤0.06 |
≤0.06 |
ZQCr5 |
2.2-3.2 |
≤1.0 |
0.3-1.5 |
4.0-6.0 |
≤1.0 |
≤0.8 |
≤1.0 |
≤0.08 |
≤0.08 |
ZQCr2 |
2.2-3.2 |
≤1.0 |
0.3-1.5 |
1.0-3.0 |
≤1.0 |
≤0.8 |
≤1.0 |
≤0.10 |
≤0.10 |
ZQCADI |
3.3-3.9 |
2.4-3.0 |
1.4-1.9 |
0.2-0.5 |
≤0.5 |
0.1-0.5 |
0.1-0.5 |
≤0.05 |
≤0.05 |
Chromium Alloy Grinding Steel Balls Specification
Specification (mm) |
Weight of Each Ball (Kg) |
Pcs/ton |
T/m³ |
φ15 |
0.017 |
58824 |
4.94 |
φ17 |
0.024 |
41667 |
4.91 |
φ20 |
0.037 |
27027 |
4.89 |
φ25 |
0.070 |
14286 |
4.87 |
φ30 |
0.110 |
9091 |
4.85 |
φ40 |
0.257 |
3891 |
4.76 |
φ50 |
0.500 |
2000 |
4.70 |
φ60 |
0.867 |
1153 |
4.66 |
φ70 |
1.070 |
729 |
4.62 |
φ80 |
2.050 |
487 |
4.60 |
φ90 |
2.900 |
345 |
4.58 |
φ100 |
4.000 |
250 |
4.56 |
φ110 |
5.300 |
188 |
4.55 |
φ120 |
6.800 |
147 |
4.54 |
φ125 |
7.750 |
129 |
4.52 |
φ130 |
8.740 |
114 |
4.50 |
Grinding Forging Chemical Compoents
Designation |
Chemical Compositions(%) |
C |
Si |
Mn |
Cr |
Mo |
P |
S |
ZDCr26 |
2.2-3.0 |
≤1.0 |
0.3-1.0 |
24.0-30.0 |
≤1.0 |
≤0.10 |
≤0.06 |
ZDCr23 |
2.2-3.0 |
≤1.0 |
0.3-1.0 |
22.0-24.0 |
≤1.1 |
≤0.10 |
≤0.06 |
ZDCr20 |
2.2-3.0 |
≤1.0 |
0.3-1.0 |
18.0-22.0 |
≤1.0 |
≤0.10 |
≤0.06 |
ZDCr17 |
2.2-3.0 |
≤1.0 |
0.3-1.0 |
16.0-18.0 |
≤1.0 |
≤0.10 |
≤0.06 |
ZDCr15 |
2.2-3.0 |
≤1.0 |
0.3-1.0 |
14.0-16.0 |
≤1.1 |
≤0.10 |
≤0.06 |
ZDCr12 |
2.2-3.0 |
≤1.0 |
0.3-1.0 |
10.0-14.0 |
≤1.0 |
≤0.10 |
≤0.06 |
ZDCr8 |
2.2-3.2 |
≤1.0 |
0.3-1.5 |
7.0-10.0 |
≤1.0 |
≤0.10 |
≤0.06 |
ZDCr5 |
2.2-3.2 |
≤1.0 |
0.3-1.5 |
4.0-6.0 |
≤1.0 |
≤0.10 |
≤0.10 |
ZDCr2 |
2.2-3.2 |
≤1.0 |
0.3-1.5 |
1.3-3.5 |
≤1.0 |
≤0.10 |
≤0.10 |
ZDCADI |
3.3-3.9 |
2.4-3.0 |
2.4-2.9 |
0.2-0.5 |
≤0.5 |
≤0.06 |
≤0.05 |
Grinding Forging Specification
Specification (mm) |
Weight of Each Ball (Kg) |
Pcs/ton |
φ8×10 |
0.0039 |
255056 |
φ10×12 |
0.0074 |
136030 |
φ12×14 |
0.0120 |
80970 |
φ14×16 |
0.0190 |
52052 |
φ16×18 |
0.0280 |
35424 |
φ18×20 |
0.0400 |
25191 |
φ20×25 |
0.0610 |
16324 |
φ25×30 |
0.1150 |
8706 |
φ30×35 |
0.1930 |
5182 |
φ35×40 |
0.3000 |
3331 |
φ40×45 |
0.4400 |
2267 |
φ45×55 |
0.5711 |
1751 |
φ55×60 |
0.8611 |
1161 |
Grinding Balls Series
![High Chrome Casting Wear Resistant Balls for Cement Plants and Metallurgical Mining](//www.micstatic.com/athena/img/transparent.png)
Designation |
HRC |
AK(J/CM²) |
Microstucture |
Falling Times |
ZQCr28 |
≥58 |
≥4.8 |
M+C |
≥18000 |
ZQCr26 |
≥58 |
≥4.8 |
M+C |
≥18000 |
ZQCr20 |
≥59 |
≥4.8 |
M+C |
≥18000 |
ZQCr15 |
≥60 |
≥4.8 |
M+C |
≥18000 |
ZQCr12 |
≥60 |
≥4.5 |
M+C |
≥18000 |
ZQCr8 |
50-65 |
≥3.5 |
P+C/M+C |
≥12000 |
ZQCr5 |
49-62 |
≥3.0 |
P+C/M+C |
≥12000 |
ZQCr2 |
≥48 |
≥3.0 |
P+C |
≥10000 |
ZQCADI |
55-60 |
≥10 |
B+Fe |
≥25000 |
C-Carbide M-Martensite P-Pearlite B-Bainite Fe-Ferrite |
Steel Forging Series
Designation |
Surface HRC |
Core HRC |
Microstucture |
ZDCr28 |
≥62 |
≥62 |
M+C |
ZDCr26 |
≥62 |
≥62 |
M+C |
ZDCr23 |
≥62 |
≥62 |
M+C |
ZDCr20 |
≥62 |
≥62 |
M+C |
ZDCr17 |
≥62 |
≥62 |
M+C |
ZDCr15 |
≥62 |
≥62 |
M+C |
ZDCr12 |
≥62 |
≥62 |
M+C |
ZDCr8 |
50-55 |
50-55 |
P+C/M+C |
ZDCr5 |
50-55 |
50-55 |
P+C/M+C |
ZDCr2 |
≥48 |
≥47 |
P+C |
ZDCADI |
55-60 |
55-60 |
B+Fe |
C-Carbide M-Martensite A-Ferrite B-Bainit Fe-Ferrite |
Liner Series
Fully Automatic Production Line
Main Production Equipments
1. 1.5 tons medium frequency induction furnace (4 SETS)
2. 2.0 tons medium frequency induction furnace (4SETS)
3. 1.0 tons medium frequency induction furnace (3 SETS)
4. Automatic iron coated sand casting production line (3SETS)